A modest method of synthesis Cu- based metal-organic frameworks using benzene dicarbocxylate as a ligan for promising candidate of flue gas CO2 adsorption

MUTTAQIN MUTTAQIN, FARID IMAM HIDAYAT

Abstract


Metal organic framework (MOF) is one of extraordinary materials in many technical field applications. One of them is as CO2 gas adsorbent. We studied, synthesized, and characterized Copper-based material, known as Metal organic frameworks (MOFs), using a solvothermal-based modification method. Copper salt (Cu (NO3)2. 3H2O) and benzene dicarboxylic acid (H2BDC) were mixed and then heated in an oven at 120°C, to produce low impurities, small pore and uniform particle size of materials called CuBDC. Infrared spectroscopy and XRD data confirmed the formation of CuBDC. Furthermore, the result showed that CuBDC frameworks have good thermal stability up to 330°C.  Thereafter SEM picture showed random, layered, and asymmetrical corners structure which is typical of triclinic crystal system. Lastly, specific surface areas and the porosity were analyzed using The Brunauer-Emmett-Teller (BET) method. It recorded 485 m2.g-1 of surface area while average pore volume and average pore size are 0.16 cm3.g-1 and 5.9 Å respectively.   @font-face {font-family:"Cambria Math"; panose-1:2 4 5 3 5 4 6 3 2 4; mso-font-charset:0; mso-generic-font-family:roman; mso-font-pitch:variable; mso-font-signature:-536869121 1107305727 33554432 0 415 0;}p.MsoNormal, li.MsoNormal, div.MsoNormal {mso-style-unhide:no; mso-style-qformat:yes; mso-style-parent:""; margin:0cm; mso-pagination:widow-orphan; font-size:12.0pt; font-family:"Times New Roman",serif; mso-fareast-font-family:"Times New Roman"; mso-ansi-language:EN-US;}.MsoChpDefault {mso-style-type:export-only; mso-default-props:yes; font-size:10.0pt; mso-ansi-font-size:10.0pt; mso-bidi-font-size:10.0pt; mso-ansi-language:IN; mso-fareast-language:IN;}div.WordSection1 {page:WordSection1;}

Keywords


MMetal Organic Framework, CCS, CuBDC, adsorbent

References


Furukawa, S.; Reboul, J.; Diring, S.; Sumida, K.; Kitagawa, S. 2014. Structuring of metal–organic frameworks at the mesoscopic/macroscopic scale. Chem. Soc. Rev. 43 5700 - 5734.

Rosi, N. L.; Kim, J.; Eddaoudi, M.; Chen, B.; O’Keeffe, M.; Yaghi, O. M. 2005. Rod packings and metal−organic frameworks constructed from rod-shaped secondary building units. J. Am. Chem. Soc. 127 1504 - 1518.

Xiang, Z.; Cao, D.; Lan, J.; Wang, W. and Broom, D.P. 2010. Multiscale simulation and modelling of adsorptive processes for energy gas storage and carbon dioxide capture in porous coordination frameworks. Energy Environ. Sci. 3 1469–1487.

Li, H.; Eddaoudi, M.; O7Keeffe, M.; Yaghi, O. M. 1999. Design and synthesis of an exceptionally stable and highly porous metal-organic framework. Nature 402 276 - 279.

Getachew, N.; Chebude, Y.; Diaz, I.; Sanchez-Sanchez, M. 2014. Room temperature synthesis of metal organic framework MOF-2. J. Porous Mater. 21, 769 – 773.

Sumida, K.; Rogow, D. L.; Mason, J. A.; McDonald, T. M.; Bloch, E. D.; Herm, Z. R.; Bae, T-H.; Long, J. R. 2012. Carbon dioxides capture in metal–organic frameworks. Chem. Rev. 112 724 – 781.

Mori, W.; Inoue, F.; Yoshida, K.; Nakayama, H.; Takamizawa, S.; Kishita, M. 1997. Synthesis of new adsorbent copper (II) terephthalate. Chem. Lett. 12 1219–1220.

Seki, K.;Takamizawa, S.; Mori, W. 2001. Design and Gas Adsorption Property of a Three-Dimensional Coordination Polymer with a Stable and Highly Porous Framwork. Chem. Lett. 30(4) 332–333.

Carson, C.G.; Brunnello, G.; Lee, S.G.; Jang, S.S.; Gerhardt, R.A.; Tannenbaum, R. 2014. Structure solution from powder diffraction of copper 1,4- benzenedicarboxylate. Eur. J. Inorg. Chem. 12 2140–2145.

Xin, Z.; Bai, J.; Shen, Y.; Pan, Y. 2010. Hierarchically Micro- and Mesoporous Coordination Polymer Nanostructures with High Adsorption Performance. Cryst. Growth Des. 10(6) 2451–2454.

Carson, C.G.; Hardcastle, K.; Schwartz, J.; Liu, X.; Hoffmann, C.; Gerhardt, R. A.; Tannenbaum, R. 2009. Synthesis and structure characterization of copper terephthalate metal-organic frameworks. Eur. J. Inorg. Chem. 16 2338–2343.

Chowdhury, P.; Bikkina, C; Meister, D; Dreisbach, F; Gumma, S. 2009.

Comparison of adsorption isotherms on Cu-BTC metal organic frameworks synthesized from different routes. Microporous Mesoporous Mater.117(1-2) 406-413.

Yang, H.; Yuan, Y.; Chi, S.; Tsang, E. 2012. Nitrogen-enriched carbonaceous materials with hierarchical micro-mesopore structures for efficient CO2 capture. Chem. Eng. J. 185–186 374–379.

Mason, J. A.; McDonald, T. M.; Bae, T-H.; Bachman, J. E.; Sumida, K.; Dutton, J. J.; Kaye, S. S.; Long, J. R. 2015. Application of a high-throughput analyzer in evaluating solid adsorbents for post-combustion carbon capture via multicomponent adsorption of CO2, N2, and H2O. J. Am. Chem. Soc. 137 4787–4803.

Lin, Y.; Kong, C.; Chen, L. 2016. Amine-functionalized metal-organic frameworks: structure, synthesis, and application. RSC Advances. 6 32598–32614.

Rodenas, T.; Luz, I.; Prieto, G.; Seoane, B.; Miro, H.; Corma, A.; Kapteijn, F.; Llabres, F. X.; Gascon, J. 2015. Metal-organic framework nanosheets in polymer composite materials for gas separation. Nat. Mater. 14 (1) 48–55.

Wee, L. M.; Lohe, M. R.; Janssens, N.; Kaskel, S.; Martens, J. A. 2015. Fine Tuning of Metal-Organic Framework Cu3(BTC)2 HKUST-1 Crystal Size in the 100 nm-5 Micron Range. J. Mater. Chem. 22(27) 13742–13747.

Mu, X.; Chen, Y.; Lester, E.; Wu, T. 2018. Optimized synthesis of nano-scale high quality HKUST-1 under mild conditions and its application in CO2 capture. Microporous Mesoporous Mater. 270 249–257.

Kareem, H. M.; Alrubaye, R. T. A. 2019. Synthesis and Characterization of Metal Organic Frameworks for Gas Storage, IOP Conf. Ser. Mater. Sci. Eng. 518 (6) 062013 – 062021.

Huang, L.; Joshi, K. L.; van Duin, A. C.; Bandosz, T. J.; Gubbsin, K. E. 2012. ReaxxFF molecular dynamics simulation of thermal stability of a Cu3(BTC)2 metal-organic framework. Microporous Mesoporous Mater. 14 (32) 11327 - 11332.

Petit, C.; Huang, L.; Jagiello, J.; Kenvin, J.; Gubbins, K. E.; Bandosz, T. J. 2011. Toward understanding reactive adsorption of ammonia on Cu-MOF/Graphite oxide nanocomposites. Langmuir. 27 13043–13051.

Mori, W.; Sato, T.; Ohmura, T.; Kato, C. N.; Takei, T. 2005. Functional microporous materials of metal carboxylate: Gas-occlusion properties and catalytic activities. J. Solid State Chem. 178 2555 - 2573.

Millward, A. R.; Yaghi, O. M. 2005. Metal-Organic frameworks with exceptionally high capacity for storage of carbon dioxide at room temperature. J. Am. Chem. Soc. 127 17998-17999.


Full Text: PDF

DOI: 10.24815/jn.v21i3.20035

Refbacks

  • There are currently no refbacks.